杜邦™聚甲醛®铃100P NC010缩醛（POM）的均聚物  
材质说明：  聚甲醛®铃100P是一种高粘度，用于填补模具容易聚缩醛。聚甲醛®铃100P提供了在不加修改的产品线最大的韧性。聚甲醛®铃100P改善了加工热稳定性 
Physical Properties Metric English Comments 
Specific Gravity  1.42 g/cc 1.42 g/cc ASTM D 792 
Density  1.42 g/cc 0.0513 lb/in³ ISO 1183 
Water Absorption  0.400 % 0.400 % Immersion 24h; ASTM D 570 
Moisture Absorption at Equilibrium  0.280 % 0.280 % Equilibrium 50%RH; ASTM D 570 
  0.300 % 0.300 % Equilibrium 50%RH; ISO 62, Similar to 
Water Absorption at Saturation  1.40 % 1.40 % Saturation; ASTM D 570 
  1.40 % 1.40 % Saturation, immersed; ISO 62, Similar to 
Linear Mold Shrinkage  0.0220 cm/cm
@Thickness 2.00 mm 0.0220 in/in
@Thickness 0.0787 in Parallel; ISO 294-4 
  0.0180 - 0.0210 cm/cm
@Thickness 3.17 mm,
Time 24.0 hour 0.0180 - 0.0210 in/in
@Thickness 0.125 in,
Time 24.0 hour Flow; ASTM D955 
Linear Mold Shrinkage, Transverse  0.0200 cm/cm
@Thickness 2.00 mm 0.0200 in/in
@Thickness 0.0787 in ISO 294-4 
  0.0170 - 0.0190 cm/cm
@Thickness 3.17 mm,
Time 24.0 hour 0.0170 - 0.0190 in/in
@Thickness 0.125 in,
Time 24.0 hour ASTM D955 
Melt Flow   1.00 g/10 min
@Load 1.05 kg,
Temperature 190 °C 1.00 g/10 min
@Load 2.31 lb,
Temperature 374 °F ASTM D 1238 
  1.90 g/10 min
@Load 2.16 kg,
Temperature 190 °C 1.90 g/10 min
@Load 4.76 lb,
Temperature 374 °F cm3/10 min; ISO 1133 
  2.50 g/10 min
@Load 2.16 kg,
Temperature 190 °C 2.50 g/10 min
@Load 4.76 lb,
Temperature 374 °F ISO 1133 
  
Mechanical Properties Metric English Comments 
Hardness, Rockwell M  92.0 92.0 ISO 2039/2 
Hardness, Rockwell R  120 120 ISO 2039/2 
  120 120 ASTM D 785 
Tensile Strength, Ultimate   31.0 MPa
@Temperature 100 °C 4500 psi
@Temperature 212 °F 5mm/min (0.2in/min); ASTM D 638 
  67.0 MPa
@Temperature 23.0 °C 9720 psi
@Temperature 73.4 °F 5mm/min (0.2in/min); ASTM D 638 
  95.0 MPa
@Temperature -40.0 °C 13800 psi
@Temperature -40.0 °F 5mm/min (0.2in/min); ASTM D 638 
Tensile Strength, Yield   26.0 MPa
@Temperature 100 °C 3770 psi
@Temperature 212 °F 5mm/min (0.2in/min); ASTM D 638 
  67.0 MPa
@Temperature 23.0 °C 9720 psi
@Temperature 73.4 °F 5mm/min (0.2in/min); ASTM D 638 
  70.0 MPa
@Temperature 23.0 °C 10200 psi
@Temperature 73.4 °F ISO 527 
  93.0 MPa
@Temperature -40.0 °C 13500 psi
@Temperature -40.0 °F 5mm/min (0.2in/min); ASTM D 638 
Elongation at Break  45.0 % 45.0 % ISO 527 
  65.0 % 65.0 % 50mm/min; ISO 527 
  40.0 %
@Temperature -40.0 °C 40.0 %
@Temperature -40.0 °F 5mm/min (0.2in/min); ASTM D 638 
..........