价格：面议
0
联系人：
电话：
地址：
Category 类 别 Trade mark 牌 号 Chemical composition 主要成份(%) Characteristics & application 特性和用途 Equivalent to AWS 相当AWS Hardfacing 硬 面 堆 焊 S 101 C3 Cr28 Ni4 Si3.5 Fe Rem. HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump. HRc48-54，耐磨、耐气蚀、抗氧化。堆焊铲斗齿，泵套 S 111 C1 Cr29 W5 Co Rem. HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve. HRc38-47，高温下耐磨、耐蚀。堆焊高温高压阀门 ECoCr-A S 112 C1.5 Cr29 W8 Co Rem. HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass. HRc45-50，高温下耐磨、耐蚀。堆焊阀门，热轧孔型 ECoCr-B S 113 C2.5 Cr30 W17 Co Rem. HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage. HRc≥55，高温下耐磨、耐热，但抗冲击性差。堆焊螺旋送料机用 S 114 C2.5 Cr30 W12 Co Rem. HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit. HRc≥53，高温下耐磨、耐热，但抗冲击较差。堆焊牙轮钻头 ECoCr-C Copper alloys 铜 合 金 S 201 Sn1 Si0.3Mn0.3 Cu Rem. Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper. 机械性能好，抗裂性好。紫铜气焊及氩弧焊用 ERCu S 211 Si3 Mn1 Cu Rem. Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel. 机械性能好，铜合金氩弧焊及钢的MIG钎焊用 ERCuSi-Al S 212 Sn5 Cu Rem. Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。铜合金氩弧焊及钢的堆焊用 ERCuSn-A S 213 Sn8 Cu Rem. Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。铜合金氩弧焊及钢的堆焊用 ERCuSn-C S 214 Al7.5 Cu Rem. Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用 ERCuAl-A1 S 215 Al9 Cu Rem. Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用 ERCuAl-A2 S 221 Cu60 Sn1 Si0.3 Zn Rem. Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔点约890℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁 S 221F Cu60 Sn1 Si 0.3 Zn Rem. S221 welding rod coated with flux. 外涂焊剂的S221焊丝 S 222 Cu58Sn0.9Si0.1 Fe0.8 Zn Rem. Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔点约880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁 RBCuZn-C S 222F Cu58Sn0.9Si0.1 Fe0.8 Zn Rem. S222 welding rod coated with flux. 外涂焊剂的S222焊丝 RBCuZn-C S 223 Cu59 Sn0.6 Zn Rem. Melting point is about 900℃. Braze welding of copper, steel and cast iron. 熔点约900℃。铜、钢、铸铁钎焊用 RBCuZn-A S 224 Cu62 Si0.5 Zn Rem. Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔点约905℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁 Copper alloys 铜 合 金 S 225 Cu48 Ni10 Zn Rem. Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys. 熔点约935℃。高强度,钎焊钢、镍及硬质合金用 RBCuZn-D S 225F Cu48 Ni10 Zn Rem. S225 welding rod coated with flux. 外涂焊剂的S225焊丝 RBCuZn-D S 226 Cu60 Sn0.3 Si0.2 Zn Rem. Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron. 熔点约900℃。黄铜气焊用，也可钎焊铜、钢、铸铁 S 227 Cu58Sn0.9Ni0.5 Si0.1 Fe0.8 Zn Rem. Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔点880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁 RBCuZn-B S 229 Cu55 Ni6 Mn4 Zn余 Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide. 熔点约920℃。高强度,钎焊钢、镍及硬质合金用 Aluminum alloys 铝 合 金 S 301 Al≥99.5 Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum. 塑性好、耐蚀。纯铝气焊、氩弧焊用 ER1100 S 311 Si5 Al Rem. Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys. 抗裂性好，通用性大。铝合金气焊、氩弧焊用。不宜用高镁合金 ER4043 S 321 Mn1.3 Al Rem. Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys. 良好的耐蚀性、可焊性及塑性。铝合金气焊、氩弧焊用 S 331 Mg5 Mn0.4 Al Rem. Corrosion resistance and high strength. Argon arc welding of aluminum alloys. 耐蚀，强度高。铝合金氩弧焊用 ER5183