价格：面议
东莞市樟木头瑞鑫塑胶原料经营部
联系人：陈
电话：13528558270
地址：东莞市樟木头塑胶原料市场
产品规格：FG2025
产品数量：
包装说明：25KG/包
关 键 词：聚甲醛
行 业：
发布时间：2015-12-15
KEP Kepital® FG2025 25% Glass Fiber Reinforced Acetal Copolymer Physical Properties Metric English Comments Density 1.59 g/cc 0.0574 lb/in³ ASTM D792 Water Absorption 0.200 % 0.200 % 24 hours at 73°C Mechanical Properties Metric English Comments Hardness, Rockwell M 95 95 ASTM D785 Tensile Strength, Yield 136.8 MPa @Thickness 3.17 mm 19840 psi @Thickness 0.125 in Elongation at Break 3.00 % @Thickness 3.17 mm 3.00 % @Thickness 0.125 in Flexural Modulus 9.03 GPa @Thickness 3.17 mm 1310 ksi @Thickness 0.125 in Flexural Yield Strength 205.2 MPa @Thickness 3.17 mm 29760 psi @Thickness 0.125 in Izod Impact, Notched 0.960 J/cm @Thickness 3.17 mm 1.80 ft-lb/in @Thickness 0.125 in Thermal Properties Metric English Comments Melting Point 203 °C 397 °F ASTM D789 Deflection Temperature at 0.46 MPa (66 psi) 164 °C 327 °F ASTM D648 Deflection Temperature at 1.8 MPa (264 psi) 163 °C 325 °F ASTM D648 Flammability, UL94 HB @Thickness 1.59 mm HB @Thickness 0.0625 in Processing Properties Metric English Comments Rear Barrel Temperature 165 - 180 °C 329 - 356 °F Middle Barrel Temperature 175 - 195 °C 347 - 383 °F Front Barrel Temperature 180 - 195 °C 356 - 383 °F Nozzle Temperature 180 - 195 °C 356 - 383 °F Melt Temperature 185 - 220 °C 365 - 428 °F Mold Temperature 70.0 - 90.0 °C 158 - 194 °F Drying Temperature 80.0 - 90.0 °C 176 - 194 °F Dry Time 3 - 4 hour 3 - 4 hour Injection Pressure 48.3 - 117 MPa 7000 - 17000 psi